Reliable Application Service for Casaverde Foamglass
1. Tank Base Bearing and Insulation for Big Volume Tank
2. Low Temperature and Cryogenic Piping, Vessel, tank and Equipment
3. Undergtound or Aboveground Steam Piping and Chilled Water Piping
4. Chilled or Hot Water Suppling Piping
5. Offing Oil Platform
6. Circulation and Dual Temperature System
7. Heating Piping and Equipment
8. Hot Oil or Asphalt Tank
9. Liquid Heat Exchanger System
10. Insulation & Acid-resistant Lining System for Chimney in Power
Plant
11. Insulation & Energy-saving for Building
Features
1. Low density, low thermal conductivity and high compressive
strength;
2. No water absorption, moisture permeability and leakage;
3. Small thermal expansion coefficient, good dimensional stability,
no deformation and no cracking;
4. Fire protection, non combustion and corrosion resistance;
5. No mildew, no mouse sniffing, pest control and microorganism;
6. It is suitable for all kinds of harsh environments such as high
temperature, deep cold, constant temperature and humidity.
7. Easy to cut, process and construct;
8. Inorganic products, no aging, no degradation of performance,
service life synchronous with buildings;
9. Recycling, innocuity, safety and environmental protection.
Performance Index
| Item | Performance Index | Test Mode |
| I | II | III | IV |
| Volume density Kg/m3 | ≤120 | ≤140 | ≤160 | ≤180 | JC/T 647 |
| Density range | ＞100 ≤120 | ＞120 ≤140 | ＞140 ≤160 | ＞160 ≤180 |
| Conductivity W/(m*k) | ≤0.042 | ≤0.045 | ≤0.058 | ≤0.062 | GB/T 10294 |
| Compressive strength (MPa) | ≥0.5 | ≥0.6 | ≥0.6 | ≥0.7 | GB/T 5486 |
| Flexural strength (MPa) | ≥0.3 | ≥0.5 | ≥0.5 | ≥0.6 |
| Tensile strength vertical to the plane(MPa) | ≥0.15 | JG149 |
| Water Absorption by Vol. (v/v),% | ≤0.5 | JC/T 647 |
| Dimensional stability % | ≤0.3 | GB/T 8811 |
| Combustibility | A1 | GB 8624 |
| Radionuclide limit | internal exposure index(Ira) | ≤1.0 | GB 6566 |
| external exposure index(Ir) | ≤1.0 |
| Property | Unit | Grade 800 | Grade 1000 | Grade 1200 | Grade 1600 |
|
| Ave. Density | kg/m3 | 120±8 | 130±8 | 140±8 | 160±10 |
| Thermal Conductivity | Ave. Value | W/(m·K) | 0.043 | 0.044 | 0.046 | 0.048 |
| Highest Single Value | (10℃) | 0.045 | 0.046 | 0.048 | 0.05 |
| Compressive Strength | Ave. Value | MPa | 0.8 | 1 | 1.2 | 1.6 |
| Lowest Single Value | 0.55 | 0.69 | 0.83 | 1.1 |
| Water Absorption by Vol. | % | ≤0.5 |
| Thermal Expansion Coefficient | 1/℃ | 9×10-6 |
| Service Temp. | ℃ | -196～+450 |
| Property | Unit | Grade 500 | Grade 700 | Grade 1400 | Grade 2400 |
|
| Ave. Density | kg/m3 | 110±8 | 115±8 | 150±10 | 220±20 |
| Thermal Conductivity | Ave. Value | W/(m·K) | 0.038 | 0.04 | 0.047 | 0.056 |
| Highest Single Value | (10℃) | 0.04 | 0.042 | 0.049 | 0.058 |
| Compressive Strength | Ave. Value | MPa | 0.5 | 0.7 | 1.4 | 2.4 |
| Lowest Single Value | 0.35 | 0.48 | 0.97 | 1.66 |
| Water Absorption by Vol. | % | ≤0.5 |
| Thermal Expansion Coefficient | 1/℃ | 9×10-6 |
| Service Temp. | ℃ | -196～+450 |
Cellular glass is a kind of inorganic rigid insulation materials,
which is non-toxic, harmless, environmentally and friendly. It can
be applied to cryogenic and high-temperature environment, and it is
the best comprehensive low-temperature thermal insulation material.
Cellular glass is not only a cold insulation but also a thermal
insulation material, which can be used from deep cold area to
thermal state. At the same time, after long-term use it will not be
deteriorated and and it plays an important role in fire prevention
and earthquake prevention. It is not only safe and reliable, but
also durable when it is used in the harsh environment of low
temperature, deep cold, underground engineering, inflammable,
explosive, humid and chemical erosion. It is known as "permanent
thermal insulation material that does not need to be replaced".
Flow of Production